ADORBOND CC - the biocompatible cobalt-chromium-based non-precious metal fusing alloy

ADORBOND® CC Blank is a dental cobalt-based metal-ceramic alloy. ADORBOND® CC Blank is free of nickel, cadmium, beryllium and lead and complies with EN ISO 22674 type 4 for applications with thin cross-sections that are exposed to very high forces, e.g. removable partial dentures, clasps, thin veneered single crowns, fixed full arch dentures or bridges with small cross-sections, bars, attachments and implant-supported superstructures.

Nem-nichtedelmetalle metall fräsen
Technical features
E-modulus  210 Gpa
Elongation at break   10 %
Density  8.3 g/cm3
Melting interval Ts-Tl  1304-1369 °C
0.2-% Yield strength Rp 0.2  490 MPa
Highest recommended firing temperature  980 °C
Coefficient of expansion 25-500 °C  13,9
Coefficient of expansion 20-600 °C  14,0

ADORBOND BC - the clinically proven biocompatible non-precious metal-ceramic alloy based on cobalt-chromium.

Technical features
E-modulus 195 Gpa   
Elongation at break  8 %   
Density 8.4 g/cm3   
Melting interval Ts-Tl
 1310-1400 °C   
0.2-% Yield strength Rp 0.2 400 MPa   
Highest recommended firing temperature 980 °C   
Coefficient of expansion 25-500 °C 14,1   
Coefficient of expansion 20-600 °C 14,4   

ADORBOND® BC Blank is a dental cobalt-based metal-ceramic alloy. ADORBOND® BC Blank is free of nickel, cadmium, beryllium and lead and complies with EN ISO 22674 type 4 for applications with thin cross-sections that are exposed to very high forces, e.g. removable partial dentures, clasps, thin veneered single crowns, fixed full arch dentures or bridges with small cross-sections, bars, attachments and implant-supported superstructures.