Adorbond LFN

Package á 25 g

High gold-containing multi-purpose alloy

66,90  excl. VAT

66,90  / g

>> Adorbond LFN Download

Type: High gold-containing precious alloy on the gold basis intended for metal-ceramic dentures or for dental casting alloy, type 4 (extra hard) 

acc. DIN EN ISO 22674

Colour: yellow
Applicable scope: Inlays, Onlays
Crowns
Small bridges
Bridges of any physiological span
Adorbond LFN Download
Composition: Au 69,90 Ag 13,30
(mass fraction in %) Pt 9,50 Cu 2,90
Rh 0,40 In 2,00
Ir 0,10 Zn 1,90
Technical specifications: Density in g/cm³ 16,1
Vickers hardness HV 5/30  as modeling alloy (s) 180 (a-s) —
as bonding alloy (s) 180 (n)190 (a-n)220
Yield strength Rp0,2 in MPa  as modeling alloy (s) 380 (a-s) —
as bonding alloy (s) 380 (n)510 (a-n)550
Elongation at break in %  as modeling alloy (s) 11 (a-s) —
as bonding alloy (s) 10 (n)10 (a-n)10
Average linear CTE 25 – 500 °C in 10-6 K-1 16,3
Average linear CTE 25 – 600 °C in 10-6 K-1 16,5
Elastic modulus in GPa 100
Melting interval in °C 920 – 1000
Processing: Preheating temp. of the casting moulds in °C 700
Casting temperature in °C 1140
Crucibles Graphite/ceramic
Curing (a-s) Not curable
(a-n) 450°C/15min
Suitable solders: Joints before ceramic firing AL 880 PF
Joints after ceramic firing AL 700 PF
Joints as modeling alloy AL 750

1) Brief description: 

     s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.

Weight 33 g