Dentalgusslegierung Adorloy DXI

Package á 25 g

High gold-containing casting alloy

65,90  excl. VAT

65,90  / g

x

Description

>> Adorloy DXI Download

Type:High gold-containing dental casting alloy on the gold basis, type 4 (extra hard) 

acc. DIN EN ISO 22674

Colour:yellow
Applicable scope:Inlays, Onlays
Crowns
Small bridges
Bridges of any physiological span
Milling, cone and attachment works 
Modeling casting
Composition:Au69,70
(mass fraction in %)Pt4,00
Pd2,00
Ir0,10
Ag13,60
Cu9,00
Zn1,60
Technical specifications:Density in g/cm³15,6
Vickers hardness HV 5/30 (s) 240       
Yield strength Rp0,2 in MPa (s) 600       
Elongation at break in % (s) 15         
Elastic modulus in GPa80
Melting interval in °C910 – 970
Processing:Preheating temp. of the casting moulds in °C700
Casting temperature in °C1120
CruciblesGraphite/ceramic
CuringNot curable 
Suitable solders:Joints as modeling alloyAL 750

1) Brief description: 

     s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.