Edelmetalllegierung Adornova LFC

Package á 25 g

High gold-containing multi-purpose alloy

68,90  excl. VAT

68,90  / g




Type:High gold-containing precious alloy on the gold basis intended for metal-ceramic dentures or for dental casting alloy, type 4 (extra hard) 

acc. DIN EN ISO 22674

Applicable scope:Inlays, Onlays
Small bridges
Bridges of any physiological span
Milling, cone and attachment works *
Modeling casting
Applicable for LCF
(mass fraction in %)Pt9,00Zn2,00
Technical specifications:Density in g/cm³16,7
Vickers hardness HV 5/30 as modeling alloy(s) 200(a-s) 210
as bonding alloy(s) 200(n) 220(a-n) 240
Yield strength Rp0,2 in MPaas modeling alloy(s) 410(a-s) 480
as bonding alloy(s) 410(n) 450(a-n) 530
Elongation at break in % as modeling alloy(s) 6(a-s) 9
as bonding alloy(s) 6(n) 8(a-n) 6
Average linear CTE 25 – 500 °C in 10-6 K-116,8
Average linear CTE 25 – 600 °C in 10-6 K-117,0
Elastic modulus in GPa90
Melting interval in °C900 – 990
Processing:Preheating temp. of the casting moulds in °C700
Casting temperature in °C1140


Suitable solders:Joints before ceramic firingAL 880 PF
Joints after ceramic firingAL 700 PF
Joints as modeling alloyAL 750

1) Brief description: 

     s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.

*) Depending on the copper content, discoloration may occur. We refer here to our document INDIFKGRX.