Dentalgusslegierung DA Bio NORM

73,90  excl. VAT

73,90  / g



>> DA Bio NORM Download

Type:High gold-containing precious metal alloy on the gold basis intended for metal-ceramic dentures or for dental casting alloy, type 3 (hard), type 4 (extra hard) for a-n

acc. DIN EN ISO 22674

Applicable scope:Inlays, Onlays
Small bridges
Middle-sized span bridges
Milling, cone and attachment works 
Modeling casting
Applicable for LCF
(mass fraction in %)Pt8,50Zn2,40
Technical specifications:Density in g/cm³16,3
Vickers hardness HV 5/30 as modeling alloy(s) 130(a-s) 150
as bonding alloy(s) 130(n) 120(a-n) 190
Yield strength Rp0,2 in MPaas modeling alloy(s) 320(a-s) 340
as bonding alloy(s) 320(n) 200(a-n) 380
Elongation at break in % as modeling alloy(s) 17(a-s) 13
as bonding alloy(s) 17(n) 15(a-n) 8
Average linear CTE 25 – 500 °C in 10-6 K-115,8
Average linear CTE 25 – 600 °C in 10-6 K-116,2
Elastic modulus in GPa100
Melting interval in °C990 – 1050
Processing:Preheating temp. of the casting moulds in °C750
Casting temperature in °C1200
Curing                               (a-s)500°C/15min
                                               (a-n)500°C/15 min
Suitable solders:Joints before ceramic firingAuroCer Lot 920 PF
Joints after ceramic firingAuroCer Lot 700 PF
Joints as modeling alloyAuroDur H Lot 750

1) Brief description: 

     s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.