ADORLOY ECO

Description

>>> GebrAnw-Dentalgrundlegierung-Adorloy-Eco.pdf <<<

Type:	Gold-reduced precious metal alloy on the gold basis intended for metal-ceramic dentures or for dental casting alloy, type 4 (extra hard)  acc. DIN EN ISO 22674
Colour:	yellow

Applicable scope:	Inlays, Onlays	●
	Crowns	●
	Small bridges	●
	Bridges of any physiological span	●
	Milling, cone and attachment works	●
	Modeling casting	●
	Applicable for LCF	●

Composition:	Au	57,00	In	4,00
(mass fraction in %)	Pd	10,00	Zn	1,40
	Ir	0,10	Sn	0,50
	Ag	27,00

Technical specifications:	Density in g/cm³	13,9
	Vickers hardness HV 5/30	as modeling alloy	(s) 210		(a-s) -
		as bonding alloy	(s) 210	(n) 230	(a-n) 250
	Yield strength Rp0,2 in MPa	as modeling alloy	(s) 420		(a-s) -
		as bonding alloy	(s) 420	(n) 550	(a-n) 520
	Elongation at break in %	as modeling alloy	(s) 4		(a-s) -
		as bonding alloy	(s) 4	(n) 3	(a-n) 3
	Average linear CTE 25 – 500 °C in 10-6 K-1	16,9
	Average linear CTE 25 – 600 °C in 10-6 K-1	17,4
	Elastic modulus in GPa	100
	Melting interval in °C	970 - 1050

Processing:	Preheating temp. of the casting moulds in °C	700
	Casting temperature in °C	1200
	Crucibles	Graphite/ceramic
	Curing	(a-s)	Not curable 450°C/15min
		(a-n)

Suitable solders:	Joints before ceramic firing	AL 920
	Joints after ceramic firing	AL 700 PF
	Joints as modeling alloy	AL 750

1) Brief description: 

     s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.