ADORNOVA ECO

Package á 25 g

Gold-reduced multi-purpose alloy

Due to the current raw material price development, all alloys are published on a daily price basis for the time being. Prices are updated every morning at 10 am.

59,40  excl. VAT

59,40  / g

Description

>> Adornova ECO Download

Type: Gold-reduced precious metal alloy on the gold basis intended for metal-ceramic dentures or for dental casting alloy, type 4 (extra hard) 

acc. DIN EN ISO 22674

Colour: light yellow
Applicable scope: Inlays, Onlays
Crowns
Small bridges
Bridges of any physiological span
Milling, cone and attachment works 
Modeling casting
Applicable for LCF
Composition: Au 38,00
(mass fraction in %) Pd 17,00
Ag 36,00
Ir   0,10
In   8,90
Technical specifications: Density in g/cm³ 12,8 
Vickers hardness HV 5/30 as modeling alloy (s) 210                        (a-s) -
as bonding alloy (s) 210     (n) 220     (a-n) 240
Yield strength Rp0,2 in MPa as modeling alloy (s) 500                 (a-s) -
as bonding alloy (s) 500 (n) 550  (a-n) 560
Elongation at break in % as modeling alloy (s) 3                     (a-s) 
as bonding alloy (s) 3 (n)  3   (a-n) 3
Average linear CTE 25 – 500 °C in 10-6 K-1 16,9
Average linear CTE 25 – 600 °C in 10-6 K-1 17,3
Elastic modulus in GPa 90
                                                Melting interval in °C                                                                                                            1020 – 1075
Processing: Preheating temp. of the casting moulds in °C 800
Casting temperature in °C 1230
Crucibles Graphite
Curing (a-s) Not curable
(a-n) 500°C/ 15 min
Suitable solders: Joints after ceramic firing AL 700 PF
Joints as modeling alloy AL 750

1) Brief description: 

     s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.