Adornova G

Package á 25 g

High gold-containing bonding alloy

 

89,90  excl. VAT

89,90  / g

Description

>> Adornova G Download

Type: High-gold containing metal-ceramic alloy on the gold basis, type 4 (extra hard)

acc. DIN EN ISO 22674

Colour: yellow

 

Applicable scope: Inlays, Onlays
Crowns
Small bridges
Large-span bridges
Milling, cone and attachment works
Modeling casting

 

Composition: Au 86,00
(mass fraction in %) Pt 11,40
Ir   0,10
In   1,00
Rh   0,90
Ta   0,40
Mn   0,20

 

Technical specifications: Density in g/cm³ 18,9
Vickers hardness HV 5/30 (s)130 (n)160 (a-n) 170
Yield strength Rp0,2 in MPa (s)300 (n)420 (a-n) 490
Elongation at break in % (s)15 (n)15 (a)12
Average linear CTE 25 – 500 °C in 10-6 K-1 14,0
Average linear CTE 25 – 600 °C in 10-6 K-1 14,3
Elastic modulus in GPa 100
Melting interval in °C 1080 – 1170

 

Processing: Preheating temp. of the casting moulds in °C 850
Casting temperature in °C 1320
Crucibles Graphite/ceramic
Curing 550°C

 

Suitable solders: Joints before ceramic firing AL 1020
Joints after ceramic firing AL 750

 

1) Brief description:

s – self-curing, n – after ceramic firing, a-s – curing from s condition

a-n – curing from n condition

 

2) All information about cured condition is given according to the alloy:

– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

Corresponding data are true under these conditions only.

 

3) The ceramic firing should be carried out according to the manufacturer's instructions.