ADORNOVA P 500

Package á 25 g

High gold-containing bonding alloy

 

89,90  excl. VAT

89,90  / g

Description

>> Adornova P 500 Download

Type: High-gold containing metal-ceramic alloy on the gold basis, type 4 (extra hard), acc. DIN EN ISO 22674 
Colour: yellow
Applicable scope: Inlays, Onlays
Crowns
Small bridges
Middle-sized bridges
Large-span bridges
Milling, cone and attachment works 
Modeling casting
Composition: Au 85,90
(mass fraction in %) Pt 11,70
Rh 0,20
Ir 0,05
Zn 1,50
Nb 0,40
Mn 0,10
In 0,10
Fe 0,05
Technical specifications: Density in g/cm³ 18,9
Vickers hardness HV 5/30  (s) 170    (n) 200    (a-n) 250
Yield strength Rp0,2 in MPa  (s) 440    (n) 490    (a-n) 620
Elongation at break in %  (s) 6        (n) 4        (a-n) 3
Average linear CTE 25 – 500 °C in 10-6 K-1 14,4 
Average linear CTE 25 – 600 °C in 10-6 K-1 14,6 
Elastic modulus in GPa 95
Melting interval in °C 1040 - 1130
Processing: Preheating temp. of the casting moulds in °C 850
Casting temperature in °C 1280
Crucibles Graphite
Curing 450°C/15min
Suitable solders: Joints before ceramic firing AL 1040 PF 
Joints after ceramic firing AL 750

1) Brief description: 

          s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.

Additional information

Weight 33 g