ADORBOND 40

Package á 25 g

Gold-reduced bonding alloy

Due to the current commodity price development, all palladium alloys are published on a daily price basis for the time being. Prices are updated every morning at 10 am.

70,87  excl. VAT

70,87  / g

Description

>> Adorbond 40 Download

Type: Gold-reduced metal-ceramic alloy on the gold basis, type 4 (extra hard)

acc. DIN EN ISO 22674

Colour: white

 

Applicable scope: Inlays, Onlays
Crowns
Small bridges
Large-span bridges
Milling, cone and attachment works
Modeling casting

 

Composition: Au 40,00
(mass fraction in %) Pd 39,40
Ag 10,00
In   8,80
Ga   1,40
Ru   0,10
Sn   0,30

 

Technical specifications: Density in g/cm³ 12,2
Vickers hardness HV 5/30 (s) 260 (n) 260 (a-n) 270
Yield strength Rp0,2 in MPa (s) 520 (n) 520 (a-n) 630
Elongation at break in % (s) 13 (n) 13 (a-n) 11
Elastic modulus in GPa 120
Average linear CTE 25 – 500 °C in 10-6 K-1 14,1
Average linear CTE 25 – 600 °C in 10-6 K-1 14,4
Melting interval in °C 1150 – 1270

 

Processing: Preheating temp. of the casting moulds in °C 900
Casting temperature in °C 1420
Crucibles Ceramic
Curing 600°C/15min

 

Suitable solders: Joints before ceramic firing AL 1060 W
Joints after ceramic firing AL 750

 

1) Brief description:

s – self-curing, n – after ceramic firing, a-s – curing from s condition

a-n – curing from n condition

 

2) All information about cured condition is given according to the alloy:

– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

Corresponding data are true under these conditions only.

 

3) The ceramic firing should be carried out according to the manufacturer's instructions.